42hxtio 3j53 Stirp Ni Span C902 Spring Permanent Magnetic Alloy Precision Elastic Parts Material Ribbon

42hxtio 3j53 Ni Span C902 Spring Permanent Magnetic Alloy
Precision Elastic Parts Material

Sheet             Thickness:0.1mm~3.5mm

Plate              Thickness:3.5mm~40.0mm
Bar                 Dia 5.0mm~Dia180.0mm

Pipe               OD 120mm~8.0mm,ID 8.0~129mm

Wire               Dia 0.1mm-Dia5.0mm

Products Application                                                                    

They are usually used for making instruments, wireless elastic sense organs, bellows, diaphragms.

Description                                                                                  

A precipitation hardenable Nickel-Iron-Chromium alloy having outstanding controllable thermoelastic coefficient characteristics
and excellent oxidation resistance in high temperature atmospheres. The alloy can be processed to have a constant modulus
of elasticity at temperatures ranging from -45 to +65oC (-50 to +150oF).

Parameter                                                                                   
TABLE 1           Cross Reference                                                                                                                                        

Contury                                        Name 1                                    Name 2                                                         

Russia                                          42HXTΙΟ                                     H42XT                                                    

USA                                              Ni-Span c902                              Elinvar

Germany                                      Ni-Span C

UK                                                Ni-Span C

Japan                                           Sumispan-3                                 EL-3                                                              

TABLE 2      Chemical Requirement                                                                             

 Element                                                                                 Composition,%                                                  

C  ≤                                                                                                0.05

Si≤                                                                                                 0.80

P≤                                                                                                  0.020

S≤                                                                                                  0.020

Mn≤                                                                                                0.80

Ni≤                                                                                                41.5-43.0

Cr                                                                                                 5.20-5.80

TI                                                                                                  2.3-2.70

Al                                                                                                  0.5-0.8

FE                                                                                                remainder                                                                        

Notes:

1.the shape and dimensions of the alloys are in compliance with YB/T5256-1993

TABLE 3            Physical Requirement                                                                                         

Property                                                                                                  Target                                                  

Density                                                                                                        8.0                

Modulus of Elasticity(E/Empa)                                                             176500-191000

Shear eleasticity(G/MPa)                                                                      63500-73500

Vickers Hardness(HV)                                                                                350-450

Staturation induction density(B600/T)                                                           0.7

Mean Coefficient of Linear Expansion20-100ºC(10^-6/K)                                 8.5

Resistivity p/(Ω°m)                                                                                         1.1                                                   

TABLE 4            Yield Strengh(after the heat treatment)                                                                           

Delivery State                                  Thickness/mm                   Yield Stength/Mpa                                        

Annealed                                          0.50-2.50                               <685

Cold rolled                                        0.50-1.00                                >885                                                              

TABLE 5            The temperature coefficient of the modulus of elasticity                     

 Aging Temperature/ºC            The temperature coefficient of the modulus of elasticityβE/(10^-6/ºC)(-6~+80ºC)

                                                                          Cold Rolling                                  Annealed                                

500                                                                      -38~15                                        +18~+12

550                                                                      -22~0                                          +10~+35

600                                                                       0~+20                                         +35~+55

650                                                                       0~+20                                         +42~+64

700                                                                       0~+20                                         +40~+60                                

750                                                                       -4~+16                                        +28~+50                                

TABLE 6            Mechanical property requirement                                                                        

Shape        Delivery State       Thickness&Diameter/mm        Tensile Strengthòb/MPa       Elongationò(%)≥    

Strip            Annealed                0.20-0.50                                    <885                                      20
Wire            Cold Drawn            0.20-3.0                                       >930